ANALISA POROSITAS BETON BERPORI BERBASIS ZEOLIT ALAM PAHAE DAN KARBON AKTIF KULIT COKLAT
DOI:
https://doi.org/10.36294/bfdhsw14Keywords:
Porous concrete, Brown Skin, Porosity, ZeoliteAbstract
Porous concrete is concrete that has cavities in its structure so that water can drain. The aim of this research is to obtain compressive strength and porosity referring to the Aci 522R-10 method using a cylindrical mold measuring 15 cm x 30 cm with a soaking age of 28 days. The highest compressive strength values were obtained in porous concrete specimens mixed with 10% brown shell with an average compressive strength value of 11.7 Mpa and porous concrete mixed with 5% zeolite with an average compressive strength of 11,6 Mpa. The lowest compressive strength of porous concrete mixed with 5% zeolite + 10% brown skin with an average compressive strength of 5.5 Mpa and concrete mixed with 10% zeolite + 5% brown skin with an average compressive strength of 5,9 Mpa. The highest porosity was obtained in the 10% zeolite mixture variation test object and the 5% zeolite mixture + 5% brown leather variation test object, namely 27,6%.
References
Marina, C., Bernaditha, dan Pujiyanto., D.A. (2020). “Pengaruh Fly Ash Terhadap Kuat Tekan Dan Porositas Beton Berpori.” Jurnal Saintis, Vol.20, No.2, 110-118.
Putri, Suriati Eka, dan Sumiati Side. (2020). “Analisis Kandungan Oksida Logam Zeolit Alam Sulawesi Selatan Teraktivasi Asam Klorida.” Sainsmat : Jurnal Ilmiah Ilmu Pengetahuan Alam, Vol.9, No.2, 159-163.
Purnamasari, Eka, dan Handayani., F. (2020). “Beton Porous Dengan Menggunakan Agregat Lokal Di Kalimantan Selatan.” Jurnal Kacapuri : Jurnal Keilmuan Teknik Sipil, Vol.3, No.1, 139-149.
By Humas, 2019. Kulit Kakao Sebagai Penyimpan Energi, https://www.uny.ac.id/id/berita/kulit-kakao-sebagai-penyimpan-energi. (Diakses Pada 20 Agustus 2024 22:17 WIB).
Fynnisa, Z., Frida, E., Susilawati, Bukit, N., dan Zebua, H.M., (2023). “The Effect of Pressure Strength of Porous Concrete on the Addition of Natural Pahae Zeolite as a Partial Replacement of Cement.” Journal of Physics: Conference Series, Vol. 2672, No.1, 1-4.